| 性能項目 | 測試條件 | 測試方法 | 數值/描述 | 單位 | |
| 機械性能 | 拉伸強度(引張強度) | ASTM D638/ISO 527 | 200 | kg/cm²(MPa)[Lb/in2] | |
| 斷裂伸長率 | ASTM D638/ISO 527 | 1.6 | % | ||
| 拉伸模量 | ASTM D638/ISO 527 | kg/cm²(MPa)[Lb/in2] | |||
| 拉伸屈服伸長率(延伸率) | ASTM D638/ISO 527 | % | |||
| 拉伸斷裂伸長率(延伸率) | ASTM D638/ISO 527 | % | |||
| 彎曲模量(彎曲彈性率) | ASTM D790/ISO 178 | 15.5 | kg/cm²(MPa)[Lb/in2] | ||
| 彎曲強度 | ASTM D790/ISO 178 | 290 | kg/cm²(MPa)[Lb/in2] | ||
| 洛氏硬度 | ASTM D785 | 122 | |||
| IZOD 缺口沖擊強度 | 1/4" 23℃ | ASTM D256/ISO 179 | 11 | kg·cm/cm(J/M)ft·lb/in | |
| 1/4" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 1/8" 23℃ | ASTM D256/ISO 179 | 45 | kg·cm/cm(J/M)ft·lb/in | ||
| 1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| Charpy沖擊強度 | 23℃ （缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| -30℃（缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 23℃（無缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| -30℃（無缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 物性性能 | 比重（密度） | ASTM D792/ISO 1183 | 1.66 | ||
| 成型收縮率 | ASTM D955 | 0.2 | % | ||
| 熔融指數（流動系數） | 200℃/5kg | ASTM D1238/ISO 1133 | g/10min | ||
| 220℃/10kg | ASTM D1238/ISO 1133 | g/10min | |||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 0.02 | % | ||
| 熱性能 | 熱變形溫度 | 退火 | ASTM D648/ISO 75 | >260 | ℃（℉） |
| 未退火 | ASTM D648/ISO 75 | ℃（℉） | |||
| 維卡軟化點 | ASTM D1525/ISO R306 | ℃（℉） | |||
| 熔點 | - | 278 | ℃（℉） | ||
| 燃燒性（率） | UL94 | V-0 | |||
| 線性膨脹系數 | ASTM D696/ISO 11359 | 2.3 | mm/mm.℃ | ||
| 電氣性能 | 介電常數 | 100HZ | ASTM D150/IEC 60250 | 3.6 | |
| 1MHZ | ASTM D150/IEC 60250 | ||||
| 體積電阻率 | ASTM D257/IEC 60093 | 1014 | Ω.cm | ||
| 表面電阻率 | ASTM D257/IEC 60093 | Ω | |||
| 耐電弧性 | ISO 14782 | ||||
| 加工條件 | 干燥條件 | ||||
| 加工溫度 | 射嘴 | ℃ | |||
| 料筒前段 | ℃ | ||||
| 料筒中段 | ℃ | ||||
| 料筒后段 | ℃ | ||||
| 熔體溫度 | ℃ | ||||
| 模具溫度 | ℃ | ||||
| 壓力 | 注塑壓力 | Mpa | |||
| 保壓壓力 | Mpa | ||||
| 背壓 | Mpa | ||||
| 螺桿轉速 | rpm | ||||
| 其他 | 備注 | ||||
| 顏色 | |||||
| 特性 | 40%加纖，增強.低光澤 | ||||
| 用途 | |||||