LCP - 7130L 物性表
LCP 7130L 美國(guó)杜邦公司 物性數(shù)據(jù) |
①原料描述部分 |
||||||
暫無(wú)此原料描述部分┄ |
||||||
②原料技術(shù)數(shù)據(jù) |
||||||
性能項(xiàng)目 |
試驗(yàn)條件[狀態(tài)] |
測(cè)試方法 |
測(cè)試數(shù)據(jù) |
數(shù)據(jù)單位 |
||
物理性能 |
比重 |
黑色 |
ASTM D-792 |
1.62 |
--- |
|
泰伯摩擦 |
--- |
ASTM D-1044 |
63 |
mg |
||
模縮率 |
流向1.6mm |
ASTM D-955 |
-0.1 |
% |
||
模縮率 |
流向3.2mm |
ASTM D-955 |
0 |
% |
||
模縮率 |
橫向1.6mm |
ASTM D-955 |
0.9 |
% |
||
機(jī)械性能 |
模縮率 |
橫向3.2mm |
ASTM D-955 |
0.8 |
% |
|
洛氏硬度 |
Scale M |
ASTM D-785 |
63 |
--- |
||
沖擊下機(jī)械性能 |
--- |
UL 746B |
210 |
ºC |
||
拉伸強(qiáng)度 |
23℃,1.6mm |
ASTM D-638 |
173 |
MPa |
||
拉伸強(qiáng)度 |
23℃,3.2mm |
ASTM D-638 |
150 |
MPa |
||
斷裂伸長(zhǎng)率 |
23℃,1.6mm |
ASTM D-638 |
1.6 |
% |
||
斷裂伸長(zhǎng)率 |
23℃,3.2mm |
ASTM D-638 |
1.7 |
% |
||
拉伸模量 |
23℃,1.6mm |
ASTM D-638 |
19306 |
MPa |
||
拉伸模量 |
23℃,3.2mm |
ASTM D-638 |
18000 |
MPa |
||
彎曲模量 |
23℃,0.8mm |
ASTM D-790 |
18000 |
MPa |
||
彎曲模量 |
23℃,1.6mm |
ASTM D-790 |
14000 |
MPa |
||
彎曲模量 |
23℃,3.2mm |
ASTM D-790 |
13100 |
MPa |
||
無(wú)缺口沖擊強(qiáng)度 |
23℃,1.6mm |
ASTM D-4812 |
840 |
j/m |
||
無(wú)缺口沖擊強(qiáng)度 |
23℃,3.2mm |
ASTM D-4812 |
555,20%NB |
j/m |
||
彎曲強(qiáng)度 |
23℃,0.8mm |
ASTM D-790 |
215 |
MPa |
||
彎曲強(qiáng)度 |
23℃,1.6mm |
ASTM D-790 |
192 |
MPa |
||
彎曲強(qiáng)度 |
23℃,3.2mm |
ASTM D-790 |
183 |
MPa |
||
壓縮強(qiáng)度 |
3.2mm |
ASTM D-695 |
89 |
MPa |
||
彎曲疲勞 |
3.2mm，69MPa |
ASTM D-671 |
2667 |
cycle |
||
IZOD沖擊強(qiáng)度 |
23℃,0.8mm |
ASTM D-256 |
400,40%NB |
j/m |
||
IZOD沖擊強(qiáng)度 |
23℃,1.6mm |
ASTM D-256 |
170 |
j/m |
||
IZOD沖擊強(qiáng)度 |
23℃,3.2mm |
ASTM D-256 |
225 |
j/m |
||
電氣性能 |
介電強(qiáng)度 |
1.6mm逐步 |
ASTM D-149 |
31 |
KV/mm |
|
介電強(qiáng)度 |
23℃,1.6mm短時(shí)間 |
ASTM D-149 |
35 |
KV/mm |
||
介電強(qiáng)度 |
23℃,3.2mm短時(shí)間 |
ASTM D-149 |
＞28 |
KV/mm |
||
表面電阻率 |
--- |
ASTM D-257 |
1×1015 |
Ω |
||
體積電阻率 |
--- |
ASTM D-257 |
1×1016 |
Ω.cm |
||
損耗因素 |
23℃,3.2mm,1×109Hz |
ASTM D-2520B |
0.004 |
--- |
||
損耗因素 |
23℃,0.8mm,1×109Hz |
ASTM D-2520B |
0.004 |
--- |
||
損耗因素 |
23℃,1.6mm,1×109Hz |
ASTM D-2520B |
0.004 |
--- |
||
損耗因素 |
23℃,0.8mm,1×103Hz |
ASTM D-150 |
0.013 |
--- |
||
損耗因素 |
23℃,3.2mm,1×103Hz |
ASTM D-150 |
0.013 |
--- |
||
損耗因素 |
23℃,0.8mm,1×106Hz |
ASTM D-150 |
0.029 |
--- |
||
損耗因素 |
23℃,3.2mm,1×106Hz |
ASTM D-150 |
0.029 |
--- |
||
介電常數(shù) |
23℃,0.8mm,1×103Hz |
ASTM D-150 |
3.9 |
--- |
||
介電常數(shù) |
23℃,3.2mm,1×103Hz |
ASTM D-150 |
4.3 |
--- |
||
介電sup>6Hz |
ASTM D-150 |
3.5 |
--- |
|||
介電常數(shù) |
23℃,3.2mm,1×106Hz |
ASTM D-150 |
3.8 |
--- |
||
介電常數(shù) |
23℃,0.8mm,1×109Hz |
ASTM D-2520B |
4.4 |
--- |
||
介電常數(shù) |
23℃,3.2mm,1×109Hz |
ASTM D-2520B |
4.3 |
--- |
||
加工性能 |
熔解溫度范圍 |
℃ |
--- |
363～371 |
--- |
|
模具溫度范圍 |
℃ |
--- |
30～95 |
--- |
||
干燥時(shí)間（除濕干燥劑） |
--- |
--- |
2 |
h |
||
干燥溫度 |
--- |
--- |
135 |
℃ |
||
加工時(shí)水氣含量 |
--- |
--- |
＜0.01 |
% |
||
熱 性 能 |
相關(guān)溫度指數(shù) |
--- |
UL 746B |
240 |
ºC |
|
熔點(diǎn) |
--- |
ASTM D-3418 |
352 |
ºC |
||
導(dǎo)熱性 |
--- |
ASTM C-177 |
0.32 |
W/m k |
||
熱變形溫度 |
--- |
ASTM D-648 |
289 |
ºC |
||
玻璃轉(zhuǎn)變溫度 |
--- |
ASTM D-3418 |
120 |
ºC |
||
外推最終融溫 |
--- |
ASTM D-3418 |
360 |
ºC |
||
其它性能 |
厚度測(cè)試 |
--- |
UL 94 |
0.75 |
mm |
|
限制氧氣指數(shù) |
3.2mm |
ASTM D-2863 |
39 |
% |
||
厚度比率 |
--- |
UL 94 |
V-0 |
--- |
||