S 223（RBCuZn-A）銅合金焊絲

Category 類別	Trade mark 牌號	Chemical composition 主要成份(%)	Characteristics & application 特性和用途	Equivalent to AWS 相當AWS
Hardfacing   硬   面   堆   焊	S 101	C3 Cr28 Ni4 Si3.5 Fe Rem.	HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump. HRc48-54，耐磨、耐氣蝕、抗氧化。堆焊鏟斗齒，泵套
	S 111	C1 Cr29 W5 Co Rem.	HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve. HRc38-47，高溫下耐磨、耐蝕。堆焊高溫高壓閥門	ECoCr-A
	S 112	C1.5 Cr29 W8 Co Rem.	HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass. HRc45-50，高溫下耐磨、耐蝕。堆焊閥門，熱軋孔型	ECoCr-B
	S 113	C2.5 Cr30 W17 Co Rem.	HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage. HRc≥55，高溫下耐磨、耐熱，但抗沖擊性差。堆焊螺旋送料機用
	S 114	C2.5 Cr30 W12 Co Rem.	HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit. HRc≥53，高溫下耐磨、耐熱，但抗沖擊較差。堆焊牙輪鉆頭	ECoCr-C
Copper alloys     銅   合   金	S 201	Sn1 Si0.3Mn0.3 Cu Rem.	Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper. 機械性能好，抗裂性好。紫銅氣焊及氬弧焊用	ERCu
	S 211	Si3 Mn1 Cu Rem.	Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel. 機械性能好，銅合金氬弧焊及鋼的MIG釬焊用	ERCuSi-Al
	S 212	Sn5 Cu Rem.	Wear resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨性好。銅合金氬弧焊及鋼的堆焊用	ERCuSn-A
	S 213	Sn8 Cu Rem.	Wear resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨性好。銅合金氬弧焊及鋼的堆焊用	ERCuSn-C
	S 214	Al7.5 Cu Rem.	Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用	ERCuAl-A1
	S 215	Al9 Cu Rem.	Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel. 耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用	ERCuAl-A2
	S 221	Cu60 Sn1 Si0.3 Zn Rem.	Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔點約890℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵
	S 221F	Cu60 Sn1 Si 0.3 Zn Rem.	S221 welding rod coated with flux. 外涂焊劑的S221焊絲
	S 222	Cu58Sn0.9Si0.1 Fe0.8 Zn Rem.	Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔點約880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵	RBCuZn-C
	S 222F	Cu58Sn0.9Si0.1 Fe0.8 Zn Rem.	S222 welding rod coated with flux. 外涂焊劑的S222焊絲	RBCuZn-C
	S 223	Cu59 Sn0.6 Zn Rem.	Melting point is about 900℃. Braze welding of copper, steel and cast iron. 熔點約900℃。銅、鋼、鑄鐵釬焊用	RBCuZn-A
	S 224	Cu62 Si0.5 Zn Rem.	Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔點約905℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵
Copper alloys 銅   合   金	S 225	Cu48 Ni10 Zn Rem.	Melting point is about 935℃and high strength. Braze welding of steel, nickel and carbide alloys. 熔點約935℃。高強度,釬焊鋼、鎳及硬質合金用	RBCuZn-D
	S 225F	Cu48 Ni10 Zn Rem.	S225 welding rod coated with flux. 外涂焊劑的S225焊絲	RBCuZn-D
	S 226	Cu60 Sn0.3 Si0.2 Zn Rem.	Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron. 熔點約900℃。黃銅氣焊用，也可釬焊銅、鋼、鑄鐵
	S 227	Cu58Sn0.9Ni0.5 Si0.1 Fe0.8 Zn Rem.	Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron. 熔點880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵	RBCuZn-B
	S 229	Cu55 Ni6 Mn4 Zn余	Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide. 熔點約920℃。高強度,釬焊鋼、鎳及硬質合金用
Aluminum alloys   鋁   合   金	S 301	Al≥99.5	Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum. 塑性好、耐蝕。純鋁氣焊、氬弧焊用	ER1100
	S 311	Si5 Al Rem.	Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys. 抗裂性好，通用性大。鋁合金氣焊、氬弧焊用。不宜用高鎂合金	ER4043
	S 321	Mn1.3 Al Rem.	Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys. 良好的耐蝕性、可焊性及塑性。鋁合金氣焊、氬弧焊用
	S 331	Mg5 Mn0.4 Al Rem.	Corrosion resistance and high strength. Argon arc welding of aluminum alloys. 耐蝕，強度高。鋁合金氬弧焊用	ER5183