Sanicro 71 是一種具有正常金屬回收率的堿性藥皮焊條，用于焊接 NiCrFe 合金、9% Ni 鋼以及用于低溫環境的鎳合金鋼。它還用于異種接頭，例如，不銹鋼和 NiCu 合金與碳鋼和鎳合金之間的焊接。Sanicro 71 具有以下特點：低飛濺 和良好的脫渣性。
STANDARDS
產品認證
– ISO: 14172: Ni6182
– AWS A5.11/ASME SFA-5.11: ENiCrFe-3
– W.Nr.: 2.4807
– TüV
APPLICATIONS
Applications for Sanicro 71 are found in constructions to be used at low temperature; e.g. Ni-steel with a Cr content of 3.5 %, 5 % and 9 % are used as well as austenitic Cr-Ni stainless steel, especially if the weld metal is to be thermoformed or stress relieved.
Sanicro 71 is suitable for joining nickel alloys such as:
The alloy can be used in air up to 1200°C (2150°F), in sulphur dioxide atmospheres up to 800°C (1470°F) and inammonia at the highest process temperature. This alloy is used for surfacing or joining where there are strictrequirements on stress corrosion resistance and for high temperature service.
®
®
– Sandvik Sanicro 30 (UNS N08800, EN 1.4558, mod Alloy 800) ®
– Sandvik Sanicro 31H (UNS N08810, EN 1.4958, Alloy 800H) ®
– Sandvik Sanicro 70 (UNS N06600, EN 2.4816, Alloy 600) ®
焊縫金屬特征
以下數據對非熱處理的全焊縫金屬有效。
C Si Mn P S Cr Ni Mo Nb Fe Cu
化學成分，wt%
≤0.05 ≤1.0 6.5 ≤0.015 ≤0.010 16 67 ≤1.5 2.5 ≤10 ≤0.5
微觀組織全焊縫金屬
全奧氏體。
機械性能
免責聲明：建議僅供參考，針對特定應用場合的焊材適用性我們需要了解實際服役條件后才能予以確認。因持續研發導致的產品
技術數據更改不會另行通知。該數據表僅適用于山特維克焊材。
溫度 C (°F) 20 (68) -196 (-320)
屈服強度，R MPa (ksi) >360 (52) -
抗拉強度，R MPa (ksi) >620 (90) -
延伸率，A % >30 -
沖擊強度，夏比 V 型 J (ft lb) >60 (44) >45
R 對應于 0.2% 塑型變形的屈服強度
o
P0.2a
m
a p0.2
耐腐蝕性能
根據 ASTM A262 practice E，在“焊態”、應力消除和固溶退火狀態下的抗晶間腐蝕性。
制造
直徑，mm (in.) 電流，A
2.50 (~3/32) 45-60
3.25 (~1/8) 70–95
4.00 (~5/32) 90-120
5.00 (~3/16) 120-150
必要時重新烘干焊條：200°C (390°F)/2 h
生產率數據
焊條直徑，mm (in.) 2.50 (~3/32) 3.25 (~1/8) 4.00 (~5/32) 5.00 (~3/16)
長度，mm (in.) 300 (~12) 350 (~14) 350 (~14) 350 (~14)
重量
kg (lb)/100 pcs 1.7 (3.7) 2.9 (6.4) 5.0 (11) 8.7 (19.1)
kg (lb)/箱 4.5 (9.9) 4.6 (10.1) 5.3 (11.7) 5.2 (2.4)
焊條數/箱 260 160 105 58
有效值
kg 焊縫金屬/kg 焊條 0.61 0.71 0.68 0.67
lb 焊縫金屬/lb 焊條 0.61 0.71 0.68 0.67
變化值
焊條/kg 焊縫金屬 94 49 29 16
焊條/lb 焊縫金屬 43 23 13 7
每根焊條在最大電流下的熔化時間 (s) 46 59 76 101
工作數據
焊接位置， 除立向下焊之外的所有焊接位置
電流/極性 直流電/焊條正極。
|
不銹鋼焊條 |
E308L-15 |
FROINOX |
C:≤0.040,Si:≤0.40,Mn:1.3,Ni:10.0,Cr:20.0,Mo≤0.20,σb:≥520,σs:≥350,δ5:≥35%,Akv:≥80(+20℃)，α相:4-8%,抗裂性能和機械性能優良 |
|
E308L-16 |
SAFINOX RCN18.8S |
C:0.025,Si:0.6,Mn:1.3,Ni:10.2,Cr:19.2,σb:550,σs:390,δ5:42%,Akv:45(-100) ℃,α相：8%，力學性能和焊接工藝性能優良，特別適合管道焊接 |
|
|
E316-15 |
SAFINOX B CND 316 |
C:0.06,Si:0.6,Mn:1.80,Ni:12.5,Cr:18.5,Mo:2.2,σb:610,σs:450,δ5:35%,Akv:90(+20℃),α相：8%，抗裂性能和機械性能優良，特別適合管道焊接 |
|
|
E316L-16 |
SAFINOXR CND18.8.3S |
C:0.022,Si:0.6,Mn:1.3,Ni:12,Cr:19.2,Mo:2.2,σb:570,σs:430,δ5:38%,Akv:40(-101℃),α相:7%,力學性能和工藝性能優良，特別適合管道焊接 |
|
|
E316L-17 |
SAFFINOXR CND316L |
C:0.018,Si:0.85,Mn:0.8,Ni:11.5,Cr:18.5,Mo:2.8,σb:590,σs:400,δ5:39%,Akv:40(-101℃),α相:9%,力學和工藝性能優良，無飛濺，自動脫渣，表面平整光潔 |
|
|
E309L-15 |
FROINOX E309L-15 |
C:≤0.04,Si:0.7,Mn:1.0,Ni:13.0,Cr:23.0,Mo:≤0.5,σb:≥520,σs:≥350,δ5:≥30%,Akv:≥60(20℃),α相：8—13%,抗裂性能優良，焊接相應級別的不銹鋼或異種鋼 |
|
|
E309L-16 |
SAFINOX R CN24.12S |
C:0.025,Si:0.5,Mn:1.4,Ni:13,Cr:23.5,σb:580,σs:460,δ5:35%,Akv:55(20℃),σ相:9%,性能優良，焊接或堆焊相應級別的不銹鋼或異種鋼 |
|
|
E310-16 |
SAFINOX RCN25.20 |
C:0.10,Si:0.75,Mn:1.70,Ni:21.0,Cr:27.0,σb:580,σs:30%,Akv:65(+20℃)，純奧氏體不銹鋼焊條，性能優良，焊接相應級別的不銹鋼 |
|
|
E2209-16,-17 |
LEXAL 22.9.3 N HR |
C:0.016,Si:1.0,Mn:1.6,Ni:9.0,Cr:22.8,Mo:3.2,N:0.16,σb:810,σs:700,δ5:22%,Akv:50(-40℃),σ相:40%,雙相鋼焊條，抗拉強度高，抗點腐蝕和抗CI離子腐蝕性能優良 |
|
|
E317-16 |
FRO INOX E 317-16 |
C:≤0.08,Si:0.70,Mn:1.00,Ni:13.Cr:20,Mo:3.5,σb: ≥550,σs:≥400,δ5≥30%,Akv:≥28(+20℃),α相:5-10%焊接工藝性能良好，用于焊接AISI317不銹鋼 |
|
|
E347-16 |
SAFINOX RCN 347 |
C:0.02,Si:0.9,Mn:0.85,Ni:10.3,Cr:20.0,Nb:0.7,σb:650,σs:490,δ5:33%,Akv:75(+20℃),α相:10%，工藝性能優良，焊接含或不含TI,NB奧氏體不銹鋼 |
|
|
E410-15 |
FRO CROM 13/L |
C:≤0.08,Si:≤0.90,Mn:≤1.0,Cr:12.0,Ni:≤0.60,Mo:≤0.5,σb:≥450,δ5:≥50%,Akv:≥47(0℃),用于焊接13%Cr的鐵素體-馬氏體 |
|
|
E385-15 |
SAFINOXR CNDU 20.25.5.S |
C:0.02,Si:0.4,Mn:1.3,Ni:25.,Cr:20,Mo:4,Cu:1.7,σb:550,σs:370,δ5:35%,Akv:70(+20℃),純奧氏體不銹鋼焊條，抗熱硫酸，冷鹽酸，和點腐蝕性能非常好，焊接904等不銹鋼 |