ABS鞋跟料臺灣臺化ABS 
AG15E1 AG15A1
產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 |
| 熔體流動速率 | 200℃×5kgf(49N) | ASTM D-1238(ISO 1133) | 1.6 | g/10min |
| 熔體流動速率 | 220℃×10kgf(98N) | ASTM D-648(ISO 75/A) | 17 | g/10min |
| 比重 | 23℃ | ASTM D-792(ISO 1183) | 1.05 | |
| 抗張強(qiáng)度 | 23℃ | ASTM D-638(ISO 527) | 510(50) | kg/cm2(MPa) |
| 彎曲模數(shù) | 23℃ | ASTM D-790(ISO 178) | 27000(2650) | kg/cm2(MPa) |
| 彎曲強(qiáng)度 | 23℃ | ASTM D-790(ISO 178) | 850(84) | kg/cm2(MPa) |
| IZOD沖擊強(qiáng)度 | 23℃ | ASTM D-256(ISO R180) | 20(196) | kg.cm/cm(J/m) |
| 洛式硬度 | 23℃ | ASTM D-785(ISO 2039/2) | R-110 | |
| 熱變形溫度 | Unanneaied 18.6kg/cm(1/2"厚) | ASTM D-648(ISO 75/A) | 89 | ℃ |
| 燃燒性 | FILE NO.E162823 | UL 94 | 1/16"HB All Color | |
| 維卡軟化點 | 1Kg load | ASTM D-1525(ISO 306) | 104 | ℃ |
| 熱變形溫度 | Annealed(8℃×8hr) | ASTM D-648(ISO 75/A) | 101 | ℃ |