ERNi-1 is intended for welding wrought and cast forms of commercially pure nickel (ASTM |
||||||
| B160, B161, B162 and B163) with the gas tungsten arc, gas metal arc and plasma arc |
| welding processes.The weld metal hasgood corrosion resistance, particularly in alkalis. | ||||||
| CLASSIFICATIONS: | ||||||
| ERNi-1 | ||||||
| AWS A5.14 | ||||||
| ASME SFA 5.14 | ||||||
| UNS N02061 | ||||||
| APPLICATIONS: | ||||||
| ERNi-1 is well suited for dissimilar welding nicluding the joining of nickel 200 and 201 to | ||||||
| stainless steel. It can also be used for joining carbon steels to copper-nickel alloys. |
| DIAMETERS: | ||||||
| 0.035 , 0.045 , 0.63 , | ||||||
| 3/32 ,1/8 , | ||||||
| 5/32 ,3/16 | ||||||
| TYPICAL | ||||||
| MECHANICAL PROPERTIES: | ||||||
| Tensile Strength (psi) 55,000 | ||||||
| Percent Elongation 20 | ||||||
| TYPICAL | ||||||
| CHEMICAL COMPOSITION: | ||||||
|
C |
Mn | P | S | Si | ||
| 0.01 | 0.01 | 0.001 | 0.001 | 0.11 | ||
| Ni | Fe | |||||
| 99.60 | 0.10 | |||||
|
ERNiFeMn-Cl which has 44 percent Nickel Alloy was developed for all position gas metal arc, |
||||||
| gas tungsten arc and high speed automatic gas metal arc welding of nodular, grey,spheroidal | ||||||
| graphite and malleable cast irons to themselces or to other materials inclduing stainless |
| steel, carbon steel,low alloy steel and varous nickel alloys.Under com pressive loading Arcos | ||||||
| 2216 work hardens making it ideal for bearing surfaces and as a cushioning layer for |
| hardsurfacing applications. |
| CLASSIFICATIONS: | ||||||
| ERNiFeMn-Cl | ||||||
| AWS A5.15 | ||||||
| ASME SFA 5.15 | ||||||
| UNS N02216 | ||||||
| APPLICATIONS: | ||||||
| ERNiFeMn-Cl has been designed for welding high strength cast irons that are used in critical | ||||||
| applications such as automotive exhaust systems, catalytic converters,and other areas that |
| demand high strength at relatively high temperatures combined with ease od fabrication. |
| DIAMETERS: | ||||||
| 0.035 , 0.045 , 0.63 , | ||||||
| 3/32 ,1/8 , | ||||||
| 5/32 ,3/16 | ||||||
| TYPICAL | ||||||
| MECHANICAL PROPERTIES: | ||||||
| Tensile Strength (psi) 85,000 | ||||||
| Yield Strength (psi) 65,000 | ||||||
| Percent Elongation 15 | ||||||
| TYPICAL | ||||||
| CHEMICAL COMPOSITION: | ||||||
| C | Mn | Ni | Fe | |||
| 0.30 | 12.30 | 42.80 | Remain | |||
| Cr | Mo | Fe | Co | |||
| 21.50 | 13.50 | 3.10 | 1.80 | |||