TM-2000模具硬化堆焊用

特    性	對沖壓模的金屬磨耗非常有效,焊金第一次為奧氏體組織,第二層為高硬度的馬氏體組織.火焰淬火鋼也可以直接堆焊. The metal stamping mould for abrasion is very effective for the first time, welding gold austenitic organization, the second is the high hardness martensite steel quenching. Flame may also directly hardfacing.
用    途	直接堆焊各種鑄鐵材的模具. All sorts of cast iron material directly surfacing of mould.
規    格	2.6￠  3.2￠  4.0￠ 5.0￠ LKE-7號鋼焊條(SUPER-7)

7號鋼焊條(SUPER-7)

特    性	耐沖擊與金屬間磨耗,直接焊于熱處理后的Cr12MoV鋼上,可全位置焊接,硬度HRC52~57. Impact resistance and metal abrasion, directly welded to the Cr12MoV after heat treatment, but the position on the steel welding, hardness HRC52-57
用    途	汽車大型模具硬面制做,冷沖模刀口焊接Auto giant mould making, cold die cutting hardfaced welding.
規    格	2.6￠  3.2￠

 GNK-7A刃口焊條

特    性	熔敷金屬具有高硬度的馬氏體組織,耐磨耗耐沖擊性能優良,硬度HRC55~58. Deposited metal of martensite with high hardness, good abrasion resistance, impact resistant performance of hardness HRC55 ~ 58.
用    途	切模,沖壓模具的刃口焊材,也可以在碳鋼上堆焊制成新工具. Cutting, welding blade of stamping mould, also can be made in the new tool steel #.
規    格	2.6￠  3.2￠  4.0￠

 

 CARBO 6W各種刃口堆焊使用

特    性	高鉻成份,耐磨耗耐龜裂性能優良,焊后硬度較高,機械加工困難. High chrome component, abrasion resistance, resistance to crack excellent performance after welding, machining difficulty high hardness.
用    途	淬火硬化模具鋼刃口的修補,適用于SKD11合金工具鋼,淬火后的模具鋼修補. Quench hardened steel blade of repair, applicable to SKD11 alloy steel, alloy after quenching repair.
規    格	2.6￠  3.2￠  4.0￠

 UTP 673工模具焊條 

特   性	Cr Mo W V多元合金鋼耐磨堆焊材料,通過熱處理可調整堆焊金屬的硬度,耐熱到550℃. Cr Mo w. v. multivariate alloy wear-resistant overlaying welding materials, heat treatment can be adjusted by the hardness and resistance buttering metal 550 degrees Celsius.
用    途	用于堆焊冷作熱作工具,模具.如壓鑄模具,鍛造工具 熱修整工具和冷切刀,可堆焊在低合金鋼上制成工具. Used for surfacing cold ReZuo tool, die casting die forging. Such as heat, cold and tool grinding tools, cutting knife can be made in the low alloy steel # tools.
規    格	2.6￠  3.2￠  4.0￠

 LKE-45號鋼焊條(SUPER-45)

特    性	中硬度鋼焊條HRC45~48 Hardness steel electrode in HRC45 ~ 48
用    途	適用于汽車模具,熱坯模,鑄鋼模耐中高溫沖擊磨耗之機件延壓部分的修補,焊層可加工. Applicable to auto mould casting mould casting, heat resistant steel, high impact abrasion of the drawing and pressing machine, welding parts repair coating can be processed.
規    格	2.6￠  3.2￠  4.0￠

 GNK-12H熱鍛模焊條

特    性	高度耐熱耐磨耗,540℃高溫依然可保持52~54HRC. High abrasion resistance, heat 1,000-degree still can keep 54HRC - 52.
用    途	用于耐熱耐磨耗硬度要求很高的鍛模或錘鍛模刃口修復.更適用于H13等熱作模具局部和型腔修復. For high hardness resistant abrasion resistance of blade forging hammer forging or repair H13 etc. More suitable for ReZuo mold cavity and local repair.
規    格	2.6￠  3.2￠  4.0￠

 BK-47F熱作沖擊磨耗

特    性	熔敷金屬為低碳合金 含Ni Cr Mo V 極具韌性,含Mo V 所以回火時抗軟化,反復冷卻加熱也能保持良好的耐熱性能. For low carbon deposited metal alloys containing Ni Cr Mo V extremely toughness, including Mo V so when the tempering softening, cooling heating can keep good heat resistance.
用    途	熱作鍛造模的修補,要求在500℃耐熱耐沖擊耐金屬間磨耗部分的堆焊. ReZuo forging repair, requirements of 500 degrees in heat resistant to abrasion resistance to impact between metal parts of the hardfacing.
規    格	2.6￠  3.2￠  4.0￠

BKH-61模具修補焊條

特    性	專為修補困難的淬火硬化型模具鋼和修補硬化堆焊缺損部分的焊接而開發設計的鈦鈣性焊條,不須要高溫預熱即可堆焊. Designed for repairing difficult quench hardened steel type and repair the defect of hardening surfacing welding and part of the design and development of titanium rod, don't need calcium temperature preheating can hardfacing.
用    途	焊補沖壓模 鍛造模 工具鋼等淬火硬化后模具材料的修補. Progressive metal stamping mould forging weld-repair after quench hardened steel mold materials etc.
規    格	2.6￠  3.2￠  4.0￠

 UTP 690高速鋼焊條

特    性	Cr Mo W V 多元合金耐磨堆焊材料,堆焊金屬具有較高的抗摩擦壓力 沖擊及高溫性能,通過熱處理可調整硬度至HRC60~64. Cr Mo w. v. multielement alloy wear-resistant overlaying welding materials and high pressure and high temperature performance impact friction, through the treatment can be adjusted to HRC60 ~ 64 hardness.
用    途	用于高速鋼切割工具的修復制造,尤其是剪切刃口和工作面的堆焊,也可以在碳鋼和低合金鋼的母材上堆焊制成新工具. HSS cutting tools for repair, especially the shear blade and made the surfacing, also can be in the carbon steel and the low alloy steel base on made new tools. #
規    格	2.6￠  3.2￠  4.0￠

 GNK-6Z高速鋼焊條

特    性	焊后硬度59~62HRC 淬火后為62～64HRC C 0.9 Cr 4.5 Mo 8 W 2 V 1.5. Weld hardness 62HRC ~ 59 after 62 ~ 64HRC quenching C 0.9 Cr 4.5 Mo 8 W 2 V 1.5.
用    途	修復高速工具鋼,如切削沖孔和刨工具,高溫沖壓工具和模具,剪切刀板軋鋼和切削工具下模的切削刃口. Repair, such as high-speed tool steel cutting planer tools, high temperature and punching moulds, stamping tools and cutting knife plate rolling and cutting tools under the mold cutting edge.
規    格	2.6￠  3.2￠  4.0￠

 

 CARBO 29/9異種鋼及難焊鋼焊條

 

特    性	溶敷金屬具有低硬度高韌性,可耐熱耐腐蝕耐沖擊磨耗. Dissolve deposited metal has low hardness and high toughness, heat corrosion resistance to impact abrasion.
用    途	適用于特殊材料的修補堆焊或者冷沖壓模具的襯焊使用. Applicable to special material repair or cold stamping mould buttering welding line.
規    格	2.6￠  3.2￠  4.0￠

 NH 29-9特種鋼堆焊

特    性	操作性極好,溶敷金屬以Fe Ni Cr為主要元素的雙層組織, ,耐酸抗氧化性優良,焊后具有硬度低高韌性,又具有耐熱耐沖擊磨耗等特點. Excellent operability, soluble metal to apply for the main elements of Fe Ni Cr layer of organization, acid oxidation resistance, excellent welding, high toughness and hardness with low abrasion resistance and impact resistance, etc.
用    途	鑄鋼的焊接,工具鋼沖壓模 高低壓鑄模 塑膠模等高裂性材料焊接和做為打底緩沖層. Steel welding steel plastic mold casting mould pressing high sexual material welding and high crack a render buffer layer.
規    格	2.6￠  3.2￠  4.0￠